产品描述
|
详细介绍：
|
AWS
|
YB5092-2005
|
焊丝化学成分（%）
|
用 途
|
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Ni
|
Mo
|
Cu
|
其它
|
|
ER307
|
H1Cr21Ni9Mn4Mo
|
0.04-0.14
|
0.30-0.65
|
3.3-4.75
|
≤0.030
|
≤0.030
|
19.5-22.0
|
8.0-10.7
|
0.5-1.5
|
≤0.75
|
|
用于装甲、集装箱的焊接
|
|
ER308
|
H08Cr21Ni10 Si
|
≤0.08
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
19.50-22.00
|
9.00-11.00
|
≤0.75
|
≤0.75
|
|
用于工作温度低于300℃的0Cr19Ni9不锈钢结构的焊接
|
|
ER309
|
H12Cr24Ni13Si
|
≤0.12
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
23.00-25.00
|
12.00-14.00
|
≤0.75
|
≤0.75
|
|
同类型不锈钢及异种钢的焊接
|
|
ER310
|
H12Cr26Ni21Si
|
0.08- 0.15
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
25.00-28.00
|
20.00-22.50
|
≤0.75
|
≤0.75
|
|
焊接高温条件下工作的同类型不锈钢、异种钢的焊接
|
|
-
|
H08Cr26Ni21
|
≤0.08
|
≤0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
25.00-28.00
|
20.00-22.50
|
≤0.75
|
≤0.75
|
|
焊接高温条件下工作的同类型不锈钢、异种钢的焊接
|
|
ER316
|
H08Cr19Ni12Mo2 Si
|
≤0.08
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
18.00-20.00
|
11.00-14.00
|
2.00-3.00
|
≤0.75
|
|
用于焊接在有机和无机酸介质中工作的0Cr18Ni12Mo2钢
|
|
H03Cr19Ni12Mo2 Si
|
≤0.030
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
18.00-20.00
|
11.00-14.00
|
2.00-3.00
|
≤0.75
|
|
用于焊接尿素及合成纤维设备
|
|
ER317
|
H08Cr19Ni14Mo3
|
≤0.08
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
18.50-20.50
|
13.00-15.00
|
3.00-4.00
|
≤0.75
|
|
用于同类型不锈钢的焊接，具有较强的抗点蚀和缝隙腐蚀的能力。
|
|
ER321
|
H08Cr19Ni10Ti
|
≤0.08
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
18.50-20.50
|
9.00-10.50
|
≤0.75
|
≤0.75
|
Ti:：9×C%-1.00
|
用于0Cr18Ni10Ti不锈钢的焊接
|
|
ER347
|
H08Cr20Ni10Nb
|
≤0.08
|
0.30-0.65
|
1.00-2.50
|
≤0.030
|
≤0.030
|
19.00-21.50
|
9.00-11.00
|
≤0.75
|
≤0.75
|
Nb：10×C%-1.00
|
用于0Cr18Ni10Ti不锈钢的焊接
|
|
ER410
|
H1Cr13
|
≤0.12
|
≤0.50
|
≤0.60
|
≤0.030
|
≤0.030
|
11.50-13.50
|
≤0.60
|
≤0.75
|
≤0.75
|
|
用于0Cr13、1Cr13钢和耐磨耐蚀钢的表面堆焊
|
| |
|
产品图片