CERAMIC FIBER BLANKET
There are 5 standard grades of ceramic fiber blankets, all of which are lightweight and thermally efficient, resulting in a material that possesses the advantages of low heat storage and complete resistance to thermal shock. Used in a variety of heat processing applications, these blankets are produced from high strength spun ceramic fiber and needled to provide exceptional handling strength. These blankets are completely inorganic and are available in a variety of densities, thickness, widths, and temperature ratings:
Commercial Grade:
Standard Grade: High purity Grade: High alumina Grade: Zirconia Grade: |
continuous use up to 800oC(1472oF)
continuous use up to 1000oC(1832oF) continuous use up to 1100oC(2012oF) continuous use up to 1200oC(2192oF) continuous use up to 1350oC(2462oF) |
Available Sizes and Packagings
Standard Density:
Standard Thicknesses: Standard Widths: Standard Packaging: |
4,6,8 lbs/cu.ft.(64,96,128 kg/m3)
1/4”,1/2”,1”,1-1/2”,2” 24” or 48” carton or bags |
Product Characteristics *Excellent handling strength *Excellent corrosion resistance *Light weight *Low thermal conductivity *Low heat storage *Heat reflectance *Excellent thermal stability *Excellent fire protection *Resiliency *Excellent hot strength *Excellent sound absorption
|
Typical Application *Furnace repair *Furnace, kiln, reformer and boiler linings *Furnace door linings and seals *Reusable insulation for steam and gas turbines *High-temperature kiln and furnace insulation *Primary reformer heater insulation *High temperature gasketing *Expansion joint seals *Glass furnace crown insulation *Field steam generator lining *Nuclear insulation applications *Thermal reactor insulation *Flexible high temperature pipe insulation
|
Specifications
TYPICAL PHYSICAL PROPERTIES
Commercial Standard High-Purity High-Alumina Zirconium
Grade Grade Grade Grade Grade
Color White White White White White Max .TEMP .USE .limit 1260 0C 1260 0C 1260 0C 1400 0C 14260C (2300 0F) (2300 0F) (2300 0F) (2552 0F) (2600 0F) Continuous USE Temp. limit : 8000C 10000C 11000C 12000C 13500C (1472 0F) (1832 0F) (2012 0F) (21920F) (24610F) Average Fiber Diameter : 3-4.5 microns 3-4.5 microns 3-4.5 microns 3-4.5 microns 3-4.5 microns Average Tensile Strength: 4 pcf . Density : 5.075 psi 5.075 psi 5.075 psi 5.075 psi 5.075 psi 6 pcf. Density; 7.250 psi 7.250 psi 7.250 psi 7.250 psi 7.250 psi 8 pcf. Density 11.600 psi 11.600 psi 11.600 psi 11.600 psi 11.600 psi Rate of linear Shrinkage (24 hrs at 10000C ) 4% -- -- -- -- (24 hrs at 11000C ) -- 3% 3% -- -- (24 hrs at 12000C ) -- -- -- 3% -- (24 hrs at 13500C ) -- -- -- -- 3% Thermal Conductivity (w/m-k): 4 pcf Density at 4000C: 0.06 0.06 0.06 -- -- 4 pcf Density at 6000C: 0.10 -- 4 pcf Density at 8000C: 0.11 0.11 0.11 0.11 4 pcf Density at 10000C -- 0.16 0.16 0.16 0.16
6pcf Density at 4000C 0.076 0.076 0.076 -- -- 6pcf Density at 6000C -- -- -- 0.126 -- 6pcf Density at 8000C 0.14 0.14 0.14 -- 0.14 6pcf Density at 10000C -- 0.20 0.20 0.20 0.20
8pcf Density at 4000C 0.09 0.09 0.09 -- -- 8pcf Density at 6000C -- -- -- 0.132 -- 8pcf Density at 8000C 0.176 0.176 0.176 -- 0.176 8p cf Density at 1000C -- 0.22 0.22 0.22 0.22
Commercial Standard High-Purity High-Alumi Zirconium Grade Grade Grade Grade GradeGrade Al2O3 44% 46% 47-49% 52-55% 39-40% SiO2 52% 51% 50-52% 44-47% 38-45% Zr O2 -- -- -- -- 15-17% Fe2O3 < 1.2% < 1.0% 0.2% 0.2% 0.2% Na2O3+K2O ≤ 0.5% ≤ 0.5% 0.2% 0.2% 0.2% |