UTFR-POC-3无卤阻燃剂在聚烯烃材料中的应用 (Application of Halogen-free Flame Retardant in Polyolefin)
氢氧化铝在无卤阻燃剂中使用量很大、一般性统计数量约占无卤阻燃剂市场50%、用途非常广泛的阻燃剂. 氢氧化铝非常广泛应用于PE、PP、EVA等聚烯烃的阻燃改性中、尤其在电线电缆业被广泛使用. 然而其使用添加量60%以上、往往使其物性变差、失去该有的物性表现. 如何兼顾物性与阻燃效果、变成大家努力的目标.
UTFR-POC-3阻燃剂, 完全跳脱对氢氧化铝作改质性的思维、或APP(多聚磷酸铵)易水解问题而作改质的手段,以无卤新材料的方向做设计、其含有气源与碳源阻燃特性、达到阻燃的效果、添加在聚烯烃材料中、以30~40%的添加量、就可以达到UL94-V0等级、是无卤阻燃剂市场中的一种创新与突破. 相信对于物性有要求且须无卤阻燃效果、会是一种很好的选择或搭配使用的材料. 尤其以PP、PE、EVA聚烯烃材料作为电线电缆的绝缘材料的市场、将是无卤阻燃剂品种中、最好的选择!
低烟无卤阻燃剂
Lower smoke/Halogen-free
Flame Retardant
Type：UTFR-POC-3
Description: Special modified char forming agent, but isn’t APP and Al(OH)3 or Mg(OH)2 to modified surface structure. Is nonvolatile white powder, thermal stability, hydrolysis resistance, insoluble in most solvents, and well compatible with polyolefin resin. This environment friendly flame retardant is conformed to Euro RoHS.
Quality：
|
Items |
Index |
|
Phosphorous (wt%) |
0.7 |
|
Nitrogen (wt%) |
38.2 |
|
pH (10% suspension) |
6.0~7.0 |
|
Initial decomposition temp. (℃) |
＞270 |
|
Average particle size (μm) |
3~6 |
|
Solubility in water (g/100 cm3) |
≦0.01 |
Application：Suitable used in injection and molding articles of PE, PP and PE-EVA. These materials compounding with UTFR-POC-3 have excellent physical properties like tensile strength, thermal stability, surface/volume resistivity, high electric strength(deeping water), blooming resistance, low shrinkage, and effective flame retardability which can reach UL-94 V0. It can satisfy most electronic wire, cable and peripheral components.
Package：20 kg/bag PE bag with moisture resistant liner.
Dosage: 30~35 wt% ( for PP + 8~12% Engage )
25~30 wt% ( for PP Homopolymer )
35~40 wt% ( for PE-EVA )
＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊＊
型号: UTFR-POC-3
说明: 有别于APP与氢氧化铝/氢氧化镁表面改质性的传统作法, 非APP或氢氧化铝/氢氧化镁
系统之新材料作为无卤阻燃剂功能. 非挥发性白色粉末, 具有良好热稳定性, 抗水解性,
不溶于大部分溶剂, 与聚烯烃树脂相容性很好, 符合欧盟RoHS环境友好之无卤阻燃剂.
Quality：
|
Items |
Index |
|
Phosphorous (wt%) |
0.7 |
|
Nitrogen (wt%) |
38.2 |
|
pH (10% suspension) |
6.0~7.0 |
|
Initial decomposition temp. (℃) |
＞270 |
|
Average particle size (μm) |
3~6 |
|
Solubility in water (g/100 cm3) |
≦0.01 |
应用: 适合于PE, PP, PE-EVA材质作射出/挤出成型之部品/棒材/板材/薄膜/线材之混炼料无卤
阻燃添加剂. 混炼UTFR-POC-3后, 相对比较其他无卤阻燃剂有良好的物性如: 抗张强
度,, 低收缩率, 电气强度(浸泡水中), 电阻性, 低介电常数, 热稳定性, 抗水解性, 抗迁
移析出性之高效无卤阻燃剂. 氢氧化铝/氢氧化镁添加量60%以上达UL-94 V0, 改质
APP系统有吸湿水解迁移析出问题, UTFR-POC-3添加量30 ~ 40%达UL-94 V0. 适用
于PE,PP, PE-EVA电子讯号线, 板材, 薄膜等.
包装: 20公斤/包, 高气密PE袋.
建议用量: 30~35 wt% ( for PP + 8~12% Engage )
25~30 wt% ( for PP Homopolymer )
35~40 wt% ( for PE-EVA )