性能
|
测试方法
|
单位
|
值
|
|
机械性能
|
|||
|
拉伸屈服强度
|
ASTM D638
|
kgf/cm2
|
690
|
|
断裂伸长率
|
ASTM D638
|
%
|
>50
|
|
弯曲模量 (1/8”)
|
ASTM D790
|
kgf/cm2
|
28,500
|
|
弯曲强度 (1/8”)
|
ASTM D790
|
kgf/cm2
|
1,050
|
|
缺口冲击强度 23℃
|
ASTM D256
|
Kgfcm/cm
|
8.5
|
|
热学性能
|
|||
|
维卡软化温度, B/50
|
ASTM D1525
|
℃
|
-
|
|
热变形温度, 4.6 kg/cm2, 6.4mm, 未退火
|
ASTM D648
|
℃
|
95
|
|
热变形温度,18.6 kg/cm2, 6.4mm, 未退火
|
ASTM D648
|
℃
|
-
|
|
物理性能
|
|||
|
比重
|
ASTM D792
|
-
|
1.18
|
|
吸水性, 24小时
|
ASTM D570
|
%
|
0.11
|
|
收缩率
|
LG Method
|
%
|
0.3 – 0.5
|
|
熔融指数, 250℃/ 2.16 kgf
|
ASTM D1238
|
g/10 min
|
20
|
|
阻燃性
|
|||
|
UL, 认证, 94 V-1
|
UL 94
|
mm
|
-
|
|
UL,认证, 94 V-2
|
UL 94
|
mm
|
-
|
|
UL,认证, 94 V-0
|
UL 94
|
mm
|
1.2
|
|
UL,认证, 5VB
|
UL 94
|
mm
|
-
|
|
UL,认证, 5VA
|
UL 94
|
mm
|
-
|
|
抗刮擦性
|
|||
|
铅笔刮擦测试, 500g
|
ASTM D3363
|
-
|
F
|
|
光学性能
|
|||
|
表面光泽 @45°
|
ASTM D528
|
-
|
98
|